中文摘要: 采用沉淀法制备出磷酸铁，将其与碳酸锂、葡萄糖混合，并掺杂适量的镁，以碳热还原法制备出磷酸铁锂正极材料。制备的磷酸铁粉体D50=2.94 μm并呈正态分布。合成的镁掺杂磷酸铁锂颗粒呈类球形，D50=2.80 μm；不同镁掺杂量的磷酸铁锂XRD谱没有显著差别。掺杂后的LiFe1-xMgxPO4/C随着x值的增加，比容量有一定的上升。当x=0.01时，0.1C放电比容量为162 mAh/g，1C放电比容量达到135 mAh/g，循环性能优异。
Abstract:Ferric phosphate was prepared by precipitation method, and then mixed with lithium carbonate, glucose and magnesium source to prepare lithium iron phosphate by carbothermic reduction method. Particle size of ferric phosphate is normal distribution with D50=2.94 μm. Mg-doped lithium iron phosphate particles have spherical shape with D50=2.80 μm. XRD patterns of synthesized lithium iron phosphate show no significant differences. Specific capacity of LiFe1-xMgxPO4/C rises with increase of value of x. Upon x=0.01, the discharge capacity of sample is 162 mAh/g at 0.1C rate and 135 mAh/g at 1C rate respectively. Excellent cycle performance is presented.
文章编号： 中图分类号：TM 912.9 文献标志码：
基金项目:中国地质调查局地质调查项目（DD20160074）子项目（D1601.6.3）
| 作者 | 单位 | |
| 李超 | 中国地质科学院矿产综合利用研究所 | lichaoatcsu@sina.com |
| 刘述平* | 中国地质科学院矿产综合利用研究所 | lsp19616@sohu.com |
| 冯雪茹 | 中国地质科学院矿产综合利用研究所 | |
| 唐湘平 | 中国地质科学院矿产综合利用研究所 |
| Author Name | Affiliation | |
| LI Chao | Institute of Multipurpose Utilization of Mineral Resources,CAGS | lichaoatcsu@sina.com |
| LIU Shu-ping | lsp19616@sohu.com | |
| FENG Xue-ru | ||
| TANG Xiang-ping |
引用文本：
李超,刘述平,冯雪茹,唐湘平.镁掺杂磷酸铁锂的碳热还原法制备及表征[J].有色金属（冶炼部分）,2018(10):60-63.
LI Chao,LIU Shu-ping,FENG Xue-ru,TANG Xiang-ping.Carbothermic Reduction Preparation and Characterization of Mg-doped Lithium Iron Phosphate[J].Nonferrous Metals (Extractive Metallurgy),2018(10):60-63.
李超,刘述平,冯雪茹,唐湘平.镁掺杂磷酸铁锂的碳热还原法制备及表征[J].有色金属（冶炼部分）,2018(10):60-63.
LI Chao,LIU Shu-ping,FENG Xue-ru,TANG Xiang-ping.Carbothermic Reduction Preparation and Characterization of Mg-doped Lithium Iron Phosphate[J].Nonferrous Metals (Extractive Metallurgy),2018(10):60-63.
关注微信公众号