废旧催化剂中多金属综合回收工艺研究
朱来东,鲁兴武,易超
(西北矿冶研究院,西北矿冶研究院,西北矿冶研究院)
Technology Study of Comprehensive Recovery of Multi Metals from Waste Catalyst
ZHU Lai-dong,LU Xing-wu and YI Chao
(Northwest Research Institute of mining and metallurgy,,)
摘要
图/表
参考文献
相似文献
本文已被:浏览 978次   下载 2007
投稿时间:2013-12-01    修订日期:2013-12-03
中文摘要: 采用二段逆流浸出—沉钒—氨溶重结晶—再提纯的工艺流程从废旧催化剂中综合回收有价金属钨、钼、钒。结果表明,控制浸出温度70 ℃,时间3.5 h,碳酸钠浓度350 g/L,液固比3∶1,钨、钼、钒浸出率均在95%以上,综合回收率可以达到90%以上。
中文关键词: 废旧催化剂        综合回收
Abstract:Tungsten, molybdenum, and vanadium were comprehensively recovered from waste catalyst with a series of processes including two-stage countercurrent leaching, vanadium precipitation, recrystallization after ammonia dissolving, and purification. The results show that leaching rate of W, Mo, V is all 95% above, and comprehensive recovery is over 90% under the optimum conditions including leaching temperature of 70 ℃, leaching time of 3.5 h, sodium carbonate concentration of 350 g/L, and ratio of liquid to solid of 3∶1.
keywords: waste catalyst  W  Mo  V  comprehensive recovery
文章编号:     中图分类号:    文献标志码:
基金项目:科技部科研院所技术开发研究专项资金(2011EG115010)
引用文本:
朱来东,鲁兴武,易超,何国才.废旧催化剂中多金属综合回收工艺研究[J].有色金属(冶炼部分),2014(7):35-37.
ZHU Lai-dong,LU Xing-wu,YI Chao,HE Guo-cai.Technology Study of Comprehensive Recovery of Multi Metals from Waste Catalyst[J].Nonferrous Metals (Extractive Metallurgy),2014(7):35-37.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
86-10-63299752/63299758

杂志信息

相关下载

期刊简介

联系我们

电话:010-63299752/63299758

传真:010-63299744

QQ:XXXXXXX

Email:ysyl@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地18区23号楼

关注微信公众号