中文摘要: 采用富氧顶吹装置模拟辉锑矿挥发熔池熔炼的行为，考察了氧气系数、初始渣Fe/SiO2、CaO含量对熔炼渣中锑含量的影响。在氧气系数为1.04、初始渣Fe/SiO2=0.94、CaO 15%的最优条件下，熔炼后渣含锑为1.8%。采用SEM-EDS对渣中锑的物相及分布行为进行了表征，发现熔渣中锑以微小的金属粒子形式存在。通过加入一定量的锑锍作为捕集剂，并在高温下对锑渣进行贫化，使渣中的锑含量由沉降前的2.36%降低至0.86%。辉锑矿可以采用富氧挥发熔池熔炼—熔炼渣高温贫化工艺进行处理。
Abstract:Volatilization behavior of stibnite was simulated by an experimental equipment of oxygen enrichment top blowing. Effects of oxygen factor, Fe/SiO2 and CaO content in initial slag on Sb content in smelting slag were studied. The results show that Sb content in smelting slag is 1.8% under the optimum conditions of oxygen factor of 1.04, Fe/SiO2=0.94, and CaO of 15%. Phase and distribution of Sb in slag were analyzed with SEM-EDS. Sb exists as micro elemental particles in the slag. Sb content in slag reduces from 2.36% to 0.86% after depletion at high temperature by adding some antimony matte as collecting agent. Stibnite can be treated by the process of oxygen enrichment bath smelting and high-temperature depletion.
文章编号： 中图分类号： 文献标志码：
基金项目:中央高校基本科研业务费专项资金资助项目（FRF-BD-18-010A，230201606500078）
| 作者 | 单位 | |
| 张家靓 | 北京科技大学冶金与生态工程学院 | jialiangzhang@ustb.edu.cn |
| 杨旭 | 北京科技大学冶金与生态工程学院 | |
| 邓卫华 | 锡矿山闪星锑业有限责任公司 | |
| 陈永强 | 北京科技大学冶金与生态工程学院 | |
| 王成彦* | 北京科技大学冶金与生态工程学院 | chywang@yeah.net |
引用文本：
张家靓,杨旭,邓卫华,陈永强,王成彦.辉锑矿富氧熔池熔炼的工艺研究[J].有色金属（冶炼部分）,2019(3):1-5.
ZHANG Jia-liang,YANG Xu,DENG Wei-hua,CHEN Yong-qiang,WANG Cheng-yan.Technical Study on Oxygen Enrichment Bath Smelting for Stibnite[J].Nonferrous Metals (Extractive Metallurgy),2019(3):1-5.
张家靓,杨旭,邓卫华,陈永强,王成彦.辉锑矿富氧熔池熔炼的工艺研究[J].有色金属（冶炼部分）,2019(3):1-5.
ZHANG Jia-liang,YANG Xu,DENG Wei-hua,CHEN Yong-qiang,WANG Cheng-yan.Technical Study on Oxygen Enrichment Bath Smelting for Stibnite[J].Nonferrous Metals (Extractive Metallurgy),2019(3):1-5.
关注微信公众号