中文摘要: 国外某选矿厂浮选所得金精矿,其中杂质元素砷、硫、铁主要以毒砂和黄铁矿的形式存在于金精矿中,多数金被包裹在硫化物中。该金精矿直接氰化浸出金浸出率仅有70.89%。对比通过碱浸、细磨和热压氧化三种不同的预处理方式后金的浸出率,最终选定酸性热压氧化浸出。在氧化矿浆浓度20%、氧分压0.7 MPa、搅拌速度600 r/min、温度160 ℃、氧化反应3 h的预处理后进行氰化浸出,金浸出率达到97.49%。
Abstract:Gold concentrates obtained by flotation from a foreign concentrator, in which the impurity elements arsenic, sulfur and iron were mainly present in form of arsenopyrite and pyrite, and most of gold was encapsulated in sulfide. Gold direct cyanide leaching rate was only 70.89%. Acidic hot-pressure oxidative leaching was selected after comparing gold leaching rates of three different pretreatment methods, i.e, alkali leaching, fine grinding and hot-pressing oxidation. Gold cyanidation leaching rate is 97.49% after pretreatment under the optimum conditions including oxidation pulp concentration of 20%, oxygen partial pressure of 0.7 MPa, stirring speed of 600 r/ min, temperature of 160 ℃, and oxidation time of 3 h.
文章编号: 中图分类号: 文献标志码:
基金项目:无
作者 | 单位 | |
张伟晓 | 灵宝灵金科技有限公司,472500 | lbljkj@126.com |
闾娟沙* | 灵宝灵金科技有限公司,472500 | 13938116525@163.com |
张济文 | 灵宝灵金科技有限公司,472500 |
Author Name | Affiliation | |
Zhang Weixiao | Lingbao Lingjin Technology Co.,Ltd.,472500 | lbljkj@126.com |
lv Juansha | 13938116525@163.com | |
Zhang Jiwen |
引用文本:
张伟晓,闾娟沙,张济文.国外某含砷难处理金矿提金工艺试验[J].有色金属(冶炼部分),2019(4):56-59.
Zhang Weixiao,lv Juansha,Zhang Jiwen.Technological Test on Abroad Arsenic Bearing Refractory Gold Mine[J].Nonferrous Metals (Extractive Metallurgy),2019(4):56-59.
张伟晓,闾娟沙,张济文.国外某含砷难处理金矿提金工艺试验[J].有色金属(冶炼部分),2019(4):56-59.
Zhang Weixiao,lv Juansha,Zhang Jiwen.Technological Test on Abroad Arsenic Bearing Refractory Gold Mine[J].Nonferrous Metals (Extractive Metallurgy),2019(4):56-59.