含金物料熔融氯化提金中试探索
梁东东, 郭持皓, 袁朝新, 李大江, 李益斌, 孙彦文
(北京矿冶科技集团有限公司)
Pilot Scale Test to Recover Gold from Gold-bearing Material by Molten Chlorination
LIANG Dong-dong, GUO Chi-hao, Yuan Chao-xin, LI Da-jiang, LI Yi-bin, SUN Yan-wen
(BGRIMM Technology Group)
摘要
图/表
参考文献
相似文献
本文已被:浏览 207次   下载 293
投稿时间:2019-04-26    修订日期:2019-04-26
中文摘要: 在小试基础上,分别对氰化尾渣和焙砂进行熔融氯化工艺中试,考察电炉工艺对不同条件的适应情况。氰化尾渣试验结果表明:添加4%~12%的氯化钙,金挥发率最高可以达到99%,渣含金可控制在0.5 g/t以下。焙砂(炉底积料)试验结果表明:原料金品位89.64 g/t,因铁硅比高,渣沉降效果差,导致渣含金2~7 g/t。工程设计过程中,应该控制原料水分、调节熔渣成分、考虑分段挥发,确保金属充分回收。
中文关键词: 氰化尾渣  焙砂  熔融  氯化挥发  中试
Abstract:Based on results of laboratory experiment, pilot scale test of molten chlorination process self-developed by BGRIMM to treat cyaniding tailings and calcine was conducted. Adaptation of electric furnace process in different conditions was investigated. The test results of cyaniding tailings show that the highest gold volatilization rate is 99% and gold content in slag can be controlled at 0.5 g/t below with addition of 4%-12% calcium chloride. The test results of calcine (bottom materials of roasting furnace) with gold content of 89.64 g/t show that gold content in slag is 2-7 g/t due to high Fe/Si ratio and poor sedimentation of slag. In order to insure sufficient metal recovery, moisture of raw material should be controlled, slag composition should be adjusted, and subsection volatilization during engineering design should be considered.
文章编号:     中图分类号:    文献标志码:
基金项目:北京矿冶科技集团有限公司科研基金(YJT2017012)
引用文本:
梁东东,郭持皓,袁朝新,李大江,李益斌,孙彦文.含金物料熔融氯化提金中试探索[J].有色金属(冶炼部分),2019(10):63-66.
LIANG Dong-dong,GUO Chi-hao,Yuan Chao-xin,LI Da-jiang,LI Yi-bin,SUN Yan-wen.Pilot Scale Test to Recover Gold from Gold-bearing Material by Molten Chlorination[J].Nonferrous Metals (Extractive Metallurgy),2019(10):63-66.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
86-10-63299752/63299758

杂志信息

相关下载

期刊简介

联系我们

电话:010-63299752/63299758

传真:010-63299744

QQ:XXXXXXX

Email:ysyl@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地18区23号楼

关注微信公众号