难处理含铷矿物热解新工艺研究
(西北矿冶研究院)
Study on New Pyrolysis Process of Refractory Rubidium-bearing Minerals
LU Xing-wu1,2, LI Shou-rong, CHENG Lian, LI Yu-lian, ZHANG En-yu, CHEN Yi-bo
(1.Northwest Research Institute of Mining and Metallurgy,Key Laboratory of new#$NBSprocess#$NBSfor non-ferrous metal smelting and#$NBSrare metal#$NBShigh utilization efficiency#$NBSin Gansu Province,Gansu Baiyin 730900;2.China)
摘要
图/表
参考文献
相似文献
本文已被:浏览 206次   下载 230
投稿时间:2019-06-26    修订日期:2019-06-28
中文摘要: 选择氯化钙为添加剂,在一定条件下发生钙与钠、钾的铝硅酸盐同晶置换,使铷形成可溶于水的碱金属氯盐。通过焙烧单因素条件试验,在添加剂量为矿物质量的1倍、950 ℃焙烧1.5 h的最优热解条件下,Rb2O回收率高于98%。
中文关键词: 难处理  含铷矿物  热解  新工艺
Abstract:Applying calcium chloride as additive, sodium-potassium aluminosilicate was replaced with calcium in a certain condition to form water-soluble alkali metal chloride. Single factor test of roasting was investigated. Recovery rate of Rb2O is 98% above under the optimum pyrolysis conditions including roasting at 950 ℃ for 1.5 h, and addition of calcium chloride of twice weight of mineral.
文章编号:     中图分类号:    文献标志码:
基金项目:国家中小企业发展专项资金资助项目(白高新发[2019]69号)
引用文本:
鲁兴武,李守荣,程亮,李俞良,张恩玉,陈一博.难处理含铷矿物热解新工艺研究[J].有色金属(冶炼部分),2019(11):22-25.
LU Xing-wu,LI Shou-rong,CHENG Lian,LI Yu-lian,ZHANG En-yu,CHEN Yi-bo.Study on New Pyrolysis Process of Refractory Rubidium-bearing Minerals[J].Nonferrous Metals (Extractive Metallurgy),2019(11):22-25.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
86-10-63299752/63299758

杂志信息

相关下载

期刊简介

联系我们

电话:010-63299752/63299758

传真:010-63299744

QQ:XXXXXXX

Email:ysyl@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地18区23号楼

关注微信公众号