中文摘要: 以LiCl-KCl为电解质体系,LaCl3为原料,利用循环伏安法、计时电位法和计时电流法研究773 K时镧离子在钨电极上的电化学还原过程。结果表明,在773 K、50%KCl-50%LiCl-2%LaCl3的熔盐体系中,镧离子在钨电极上还原是一步转移3个电子反应(La3++3e →La),相对于Ag/AgCl电极析出电位为-2.05 V;镧在钨电极析出过程中出现成核极化现象,且通过循环伏安和计时电流法可判断镧离子在钨电极上的析出还原过程为受扩散控制的准可逆反应,扩散系数D=6.36×10-5 cm2/s。
中文关键词: 镧 氯化镧 LiCl-KCl熔盐 电化学还原 扩散控制
Abstract:Electrochemical reduction mechanism of La3+ on tungsten electrode at 773 K was studied through cyclic voltammetry, chronopotentiometry and chronoamperometry applying LiCl-KCl and LaCl3 as molten salt and raw material. The results show that electrochemical reduction of La3+ on tungsten electrode is a three-electron transition process by one step in 50%KCl-50%LiCl-2%LaCl3 molten salt at 773 K. Electrode reaction is La3++3e →La and reduction potential of La3+ is -2.05 V(vs. Ag/AgCl) on tungsten electrode. Nuclear polarization phenomenon is observed during depositing process. Depositing process of La is a quasi-reversible reaction. Cyclic voltammetry and chronoamperometry indicate that reduction of La3+ on tungsten electrode process in 50%KCl-50%LiCl-2%LaCl3 molten salt at 773 K is controlled by diffusion step of ions with diffusion coefficient of 6.36×10-5 cm2/s.
keywords: lanthanum lanthanum chloride LiCl-KCl eutectic molten salt electrochemical reduction diffusion control
文章编号: 中图分类号: 文献标志码:
基金项目:国家自然科学基金资助项目(51664022)
作者 | 单位 | |
李林山* | 铜陵有色金属集团控股有限公司 | ly710561824@163.com |
赵宇娟 | 铜陵有色金属集团控股有限公司 | |
杨少华 | 江西理工大学 |
Author Name | Affiliation | |
LI Linshan | Tongling Nonferrous Metal Group Holdings Co.,Ltd. | ly710561824@163.com |
ZHAO Yujuan | ||
YANG Shaohua |
引用文本:
李林山,赵宇娟,杨少华.LiCl-KCl熔盐La3+在钨电极上 的电化学还原机理[J].有色金属(冶炼部分),2020(3):60-65.
LI Linshan,ZHAO Yujuan,YANG Shaohua.Electrochemical Reduction Mechanism of La3+ on Tungsten Electrode in LiCl-KCl Molten Salt[J].Nonferrous Metals (Extractive Metallurgy),2020(3):60-65.
李林山,赵宇娟,杨少华.LiCl-KCl熔盐La3+在钨电极上 的电化学还原机理[J].有色金属(冶炼部分),2020(3):60-65.
LI Linshan,ZHAO Yujuan,YANG Shaohua.Electrochemical Reduction Mechanism of La3+ on Tungsten Electrode in LiCl-KCl Molten Salt[J].Nonferrous Metals (Extractive Metallurgy),2020(3):60-65.