中文摘要: 玉林胜果寺古代冶铸遗址位于广西玉林市兴业县龙安镇杨前村胜果寺附近的丘陵，面积超过2 000 m2。采用扫描电镜及能谱分析（SEM-EDS）、金相和矿相等研究方法，对胜果寺古代冶铸遗址的5个冶金遗物炉渣样品进行成分和显微组织分析检测。结果表明，该遗址为生铁冶铸遗址，炼渣属锰硅铝系高锰炉渣。冶炼产品除供本地铸锅等生产生活用品外，大量运往韶州涔水场浸铜。
Abstract:Shengguosi ancient iron smelting and casting site with area of 2 000 m2 above is located on hillside of Shengguosi near Yangqiancun village of Long’an town, Xingye County, Yulin City, Guangxi Zhuang Autonomous Region. Composition and microstructure of five slag samples collected from the site are analyzed with metallographic microscopy, mineralographic microscopy, and SEM-EDS. The results show that it is an ancient iron smelting and casting site, and slag is mainly composed of MnO-SiO2-Al2O3. Smelting products of cast iron are transported to Censhuichang in Shaozhou of Guangdong province for copper hydrometallurgy besides for local cast pot and other productions of daily use.
keywords: Lingnan area historical metallurgy Tang and Song dynasties cast iron smelting high manganese slag copper hydrometallurgy
文章编号： 中图分类号： 文献标志码：
基金项目:国家自然科学基金资助项目(51674004)；国家社会科学基金重大项目（17ZDA178）；广西民族大学人才引进科研启动项目（2019SKQD10）
| 作者 | 单位 | |
| 黄全胜* | 广西民族大学 科技史与科技文化研究院 | chainsun@126.com |
| 黄谦玺 | 东北农业大学 金融系 | |
| 李延祥 | 北京科技大学 冶金与材料史研究所 | liyanxiang@metall.ustb.edu.cn |
| 李建西 | 陕西省考古研究院 |
引用文本：
黄全胜,黄谦玺,李延祥,李建西.广西玉林胜果寺古代冶铸遗址研究[J].有色金属（冶炼部分）,2020(8):99-106.
HUANG Quan-sheng,HUANG Qian-xi,LI Yan-xiang,LI Jian-Xi.Studuy on Ancient Iron Smelting and Casting Site at Shengguosi in Yulin, Guangxi Region[J].Nonferrous Metals (Extractive Metallurgy),2020(8):99-106.
黄全胜,黄谦玺,李延祥,李建西.广西玉林胜果寺古代冶铸遗址研究[J].有色金属（冶炼部分）,2020(8):99-106.
HUANG Quan-sheng,HUANG Qian-xi,LI Yan-xiang,LI Jian-Xi.Studuy on Ancient Iron Smelting and Casting Site at Shengguosi in Yulin, Guangxi Region[J].Nonferrous Metals (Extractive Metallurgy),2020(8):99-106.
关注微信公众号