废旧锂电池材料热解性能研究
郑朝振, 周起帆, 黄胜, 闫丽, 秦树辰, 邓超群
(矿冶科技集团有限公司)
Research on Pyrolysis Performance of Waste Lithium Battery Materials
Zheng Chao-zhen, ZHOU Qi-fan, HUANG Sheng, YAN Li, QIN Shu-chen, DENG Chao-qun
(BGRIMM)
摘要
图/表
参考文献
相似文献
本文已被:浏览 46次   下载 27
投稿时间:2020-11-03    修订日期:2020-11-10
中文摘要: 废旧锂电池作为一种二次资源有着巨大的回收价值。运用热重分析手段,通过逐个对锂电池拆解物料进行差热分析,确定各类电池材料的高温破坏温度特性,并在此基础上开展了废旧锂电池的热解试验。结果表明,在400 ℃热解可获得良好的热解效果,黑粉回收率>97%。
中文关键词: 废旧锂电池  热解  极片  黑粉        
Abstract:As a secondary resource, waste lithium batteries have big recovery value. Thermogravimetric analysis was used to determine high temperature destruction temperature characteristics of various battery materials through differential thermal analysis of lithium battery dismantling materials one by one. On this basis, pyrolysis test of waste lithium batteries was carried out. The results show that good pyrolysis results can be obtained by pyrolysis at 400 ℃, and black powder recovery rate is >97%.
文章编号:     中图分类号:    文献标志码:
基金项目:国家重点研发计划项目(2018YFC1903103)
Author NameAffiliationE-mail
Zheng Chao-zhen BGRIMM 15810820585@139.com 
ZHOU Qi-fan   
HUANG Sheng   
YAN Li   
QIN Shu-chen   
DENG Chao-qun   
引用文本:
郑朝振,周起帆,黄胜,闫丽,秦树辰,邓超群.废旧锂电池材料热解性能研究[J].有色金属(冶炼部分),2021(4):102-107.
Zheng Chao-zhen,ZHOU Qi-fan,HUANG Sheng,YAN Li,QIN Shu-chen,DENG Chao-qun.Research on Pyrolysis Performance of Waste Lithium Battery Materials[J].Nonferrous Metals (Extractive Metallurgy),2021(4):102-107.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
86-10-63299752/63299758

杂志信息

相关下载

期刊简介

联系我们

电话:010-63299752/63299758

传真:010-63299744

QQ:XXXXXXX

Email:ysyl@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地18区23号楼

关注微信公众号