低品位富铁铝土矿烧结熟料浸出行为
何毅1, 周龑1, 王奕博2, 潘晓林2, 于海燕2
(1.中国有色金属建设股份有限公司;2.东北大学 冶金学院)
Leaching of Sintering Clinker from Low-grade and Iron-rich Bauxite
HE Yi1, ZHOU Yan, WANG Yibo, PAN Xiaolin2, YU Haiyan
(1.China Nonferrous Metal Industry’s Foreign Engineering & Construction Co., Ltd;2.Northeastern University)
摘要
图/表
参考文献
相似文献
本文已被:浏览 395次   下载 124
投稿时间:2024-05-14    修订日期:2024-06-08
中文摘要: 随着我国铝土矿品位的逐年降低,拜耳法很难满足氧化铝生产要求,烧结法的优势日益突出,而熟料浸出是烧结法生产氧化铝的关键工序,直接影响氧化铝浸出率、碱耗、赤泥沉降性能等技术经济指标。因此,本研究以低品位富铁铝土矿烧结熟料为原料,系统考察浸出工艺参数对熟料浸出性能的影响及其机理。结果表明,浸出液分子比、苛碱浓度、碳碱浓度和浸出温度、时间、液固比均能影响熟料浸出性能;矿石中氧化铁含量提高能够降低烧结熟料氧化铝浸出率,但降低幅度不大;在分子比1.25、苛碱浓度40 g/L、碳碱浓度25 g/L、浸出温度80 ℃、浸出时间20min、液固比5的最佳浸出条件下,低品位富铁铝土矿烧结熟料Al2O3和Na2O浸出率可分别达到85%和95%以上。
中文关键词: 低品位铝土矿  熟料  浸出  氧化铝  烧结法
Abstract:As the bauxite grade in China decreases year by year, it is difficult for Bayer method to meet the requirements of alumina production, while the advantages of sintering method are becoming increasingly prominent. Clinker leaching is a key process in the production of alumina by the sintering method, which directly affects the technical and economic indicators such as alumina leaching rate, alkali consumption and red mud settling performance. Therefore, the effects of the leaching parameters on the leaching rates of Al2O3 and Na2O during the leaching process were studied using the sintering clinker from low-grade and iron-rich bauxite. The results show that molecular ratio, caustic concentration, carbonate concentration of leaching solution, leaching temperature, time, and liquid-solid ratio can all affect the leaching performance of clinker; the increase of iron oxide content in bauxite can reduce the alumina leaching rate of sintered clinker, but the reduction is not significant. The leaching rate of Al2O3 and Na2O in the sintering clinker can reach over 85% and 95%, respectively, under the optimum leaching conditions including molecular ratio of 1.25, caustic concentration of 40 g/L, carbonate concentration of 25 g/L, leaching temperature of 80 ℃, leaching time of 20 min and liquid-solid ratio of 5.
文章编号:     中图分类号:    文献标志码:
基金项目:国家自然科学基金资助项目(22078055)
引用文本:
何毅,周龑,王奕博,潘晓林,于海燕.低品位富铁铝土矿烧结熟料浸出行为[J].有色金属(冶炼部分),2024(12):43-49.
HE Yi,ZHOU Yan,WANG Yibo,PAN Xiaolin,YU Haiyan.Leaching of Sintering Clinker from Low-grade and Iron-rich Bauxite[J].Nonferrous Metals (Extractive Metallurgy),2024(12):43-49.

我们一直在努力打
造,精品期刊,传
播学术成果

全国咨询服务热线
86-10-63299752/63299758

联系我们

电话:010-63299752/63299758

传真:010-63299744

QQ:XXXXXXX

Email:ysyl@bgrimm.com

邮编:100160

地址:北京市南四环西路188号总部基地18区23号楼

关注微信公众号