中文摘要: 采用自行研制的球磨装置对三水铝石矿进行了球磨溶出工艺研究。考察了填充系数，转速，料球比，配矿量和溶出温度等因素对球磨溶出性能的影响，并对球磨溶出矿浆进行了XRD分析。结果表明，三水铝石矿的最佳球磨工艺为：装球量30%，钢弹转速100 r/min，料球比1.2∶1，球磨钢球采用混合球(2~20 mm)，100 mL母液配矿量25 g，溶出温度150 ℃。
Abstract:Ball milling digestion techniques on gibbsite were studied using ball milling device designed by ourselves. Effects of fill ratio, rotation speed, the ratio of slurry and balls, ore amount and temperature on digestion properties were investigated. The dissolved slurry was analyzed by XRD. The results showed that the optimal ball milling techniques on gibbsite include rate of ball amount rate of 30%, rotation speed of 100 r/min, the ratio of slurry and balls of 1.2∶1, mixed balls with the size from 2 mm to 20 mm and digesting temperature of 150 ℃.
keywords: Ball milling Gibbsite Digestion properties Rotate speed
文章编号： 中图分类号： 文献标志码：
基金项目:国家自然科学基金资助项目(50874061)
引用文本：
王一雍,金辉,李继东,李静.球磨-浸出工艺处理三水铝石矿的工艺研究[J].有色金属（冶炼部分）,2011(4):19-22.
WANG Yi-yong,JIN Hui,LI Ji-dong,LI Jing.Study of Ball Milling Digestion on Gibbsite[J].Nonferrous Metals (Extractive Metallurgy),2011(4):19-22.
王一雍,金辉,李继东,李静.球磨-浸出工艺处理三水铝石矿的工艺研究[J].有色金属（冶炼部分）,2011(4):19-22.
WANG Yi-yong,JIN Hui,LI Ji-dong,LI Jing.Study of Ball Milling Digestion on Gibbsite[J].Nonferrous Metals (Extractive Metallurgy),2011(4):19-22.
关注微信公众号