中文摘要: 采用高温固相反应法，在1 400 ℃/12 h烧结条件下制备了具有Ti空位补偿的Ba1-xSmxTi1-x/4O3（BST；x=0.02~0.07）陶瓷。利用XRD对BST陶瓷的晶体结构进行表征，并在532和638 nm两种激发波长下对其进行拉曼光谱测试。结果表明：当x≤0.07时，所有的BST陶瓷均表现为单相钙钛矿结构，并且随着Sm含量的增加，其晶体结构由四方相（x≤0.06）转变为立方相（x=0.07）；不同激发波长下的拉曼测试证实高频谱来自稀土Sm3+的荧光效应。
Abstract:Ba1-xSmxTi1-x/4O3 (BST) (x=0.02-0.07) ceramics with Ti vacancy compensation were prepared using high temperature solid state reaction at 1 400 ℃/12 h. Crystal structure of BST ceramics was characterized by XRD, and Raman spectra were measured at 532 and 638 nm excitation wavelengths. The results show that all samples are single-phase perovskite structure when x≤0.07, and crystal structure changes from tetragonal (x≤0.06) to cubic (x=0.07). Raman spectra excited by different lasers confirm that high-frequency spectra are related to fluorescent effect of Sm3+.
keywords: BaTiO3 Sm-doped single phase fluorescent effect
文章编号： 中图分类号： 文献标志码：
基金项目:吉林省发改委项目（2019C044-1）
| 作者 | 单位 | |
| 刘巧丽 | 吉林化工学院 材料科学与工程学院 | liuqiaoli234@163.com |
| 刘军伟 | 吉林化工学院 材料科学与工程学院 | |
| 王辰 | 吉林化工学院 材料科学与工程学院 | wc23jp2@163.com |
| 路大勇* | 吉林化工学院 材料科学与工程学院 | dylu@jlict.edu.cn |
引用文本：
刘巧丽,刘军伟,王辰,路大勇.单相Sm掺杂BaTiO3陶瓷的结构研究[J].有色金属（冶炼部分）,2020(3):75-78.
LIU Qiao-li,LIU Jun-wei,WANG Chen,LU Da-yong.Structure of Single-phase Sm-doped BaTiO3 Ceramics[J].Nonferrous Metals (Extractive Metallurgy),2020(3):75-78.
刘巧丽,刘军伟,王辰,路大勇.单相Sm掺杂BaTiO3陶瓷的结构研究[J].有色金属（冶炼部分）,2020(3):75-78.
LIU Qiao-li,LIU Jun-wei,WANG Chen,LU Da-yong.Structure of Single-phase Sm-doped BaTiO3 Ceramics[J].Nonferrous Metals (Extractive Metallurgy),2020(3):75-78.
关注微信公众号